Search This Supplers Products:steel wireAlloy Steel BarSteel TubeSpring Steel StripSteel Platespring steel wire
- Home
- About us
- Products
- Faqs
- Steelmaking
- Metal Forming
- Heat Treatment
- Metal Cutting
- Surface Treatment
- Company Policy
- Another Downstream Industry Technology
- Carbon Steel
- Stainless Steel
- Alloy Steel
- Springs Industry
- Cutting Tool Industry
- Tool Steel
- High Speed Steel
- Drill Tool Industry
- Oil and Gas
- Boiler Industry
- Bearing Industry
- Auto Parts Industry
- Fasteners Industry
- Experiment Ways
- Nickel Based Alloy
- News
- Certificate
- Contact us
1.2345 X50CrVMo51 Hot Work Tool Steel
- group name
- Tool Steel Bars
- Min Order
- 1 piece
- brand name
- fushun
- Nearest port for product export
- Tianjin, Qingdao, Shanghai, Huangshi
- Delivery clauses under the trade mode
- FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
- Acceptable payment methods
- T/T, L/C, D/P D/A
- update time
- Tue, 23 May 2023 11:02:39 GMT
Paramtents
Process hot rolled or hot forged
Delivery Condtion annealed
Surface Condition smooth, bright
Packging & Delivery
-
Min Order1 piece
Briefing
Detailed
1.2345 X50CrVMo51 Hot Work Tool Steel
1.2345 is a 5%chromium hot work tool steel designed particularly for applications requiring extreme toughness combined with good red hardness.It provides an extra margin of safest in tools subject to heavy hammer blows,and those tools containing deep recesses or sharp corners.While 1.2345 has been designed primarily as a hot work tool steel,it has been used in many cold work applications where extra toughness is required at the sacrifice of some wear resistance.
Applications
1.2345 has been used primarily for tools requiring resistance to softening at elevated temperatures.Such tools include forging dies and punches,die-casting dies,aluminium extrusion dies,hot heading dies,piercing and forming punches,etc.
Chemical composition (wt.%)
C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) |
0.48-0.53 | 0.80-1.10 | 0.20-0.40 | Max 0.030 | Max 0.030 | 4.80-5.20 | 1.25-1.45 | 0.80-1.00 |
Mechanical Properties
Rp0.2 (MPa) | Rm (MPa) | Impact | Elongation | A Z (%) | Delivery | Hardness HB |
421 (≥) | 737 (≥) | 42 | 22 | 34 | Solution & Aging, Ann, Ausaging, Q+T | 321 |
Physical properties(average values)at ambient temperature
Modulus of elasticity[103x N/mm]:215
Density [g/cm3]:7.70
Thermal conductivity[W/m.K]:25.0
Electric resistivity[Ohm mm/m]:0.52
Specific heat capacity[J/g.K]:0.46
Soft Annealing
Heat to 760-8200C,cool slowly in furnace.This will produce a maximum Brinell hardness of 250.
Stress Relieving
To relieve machining strains for greater accuracy in hardening,first rough machine,then anneal below the critical 649/677C a minimum of one hour at temperature,and cool very slowly,
followed by finish machining.
Hardening
Harden from a temperature of 1000-1040C followed by air,oil warm bath(450-550%C) quenching.Hardness after quenching is 54-58 HRC.
Forging
Heat slowly and uniformly to a temperature of between 1093/1135C and forge.Do not work the steel below 927C.Reheat as often as necessary.
Machinability
The machinability of 1.2345 may be rated between 55%and 65%of a 1%carbon water hardening tool steel,or about 40%to 50%of B1112.
Weldability
To salvage tools and dies by welding,preheat to 538c in a furnace and weld with uncoated arc equipment(atomic hydrogen or heliarc).Keep the temperature of the die above 316C at all times by reheating until the welding is completed.Upon completion of the weld,return the work piece to the preheating furnace,equalize,and cool in the furnace.Welding should be performed in the annealed condition.However,if welding is performed in the hardened condition,the tool should be retempered at 538C after hardening.The electrode material used in the weld rod should be of similar analysis to the base material.