1.2601 X165CrMoV12 Cold Work Tool Steel

group name: Tool Steel Bars

Min Order: 1 piece

brand name: fushun

model: 1.2601 X165CrMoV12

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Tue, 25 Apr 2023 11:16:35 GMT

contact supplier

Paramtents

Process hot rolled or hot forged
Delivery Condtion annealed
Surface Condition smooth, bright

Packging & Delivery

Min Order1 piece

Briefing

1.2601 X165CrMoV12 Cold Work Tool Steel Bar

Detailed

1.2601 X165CrMoV12 Cold Work Tool Steel

X165CrMoV12 1.2601 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belong to DIN 17350 standard. Digital Grade material number 1.2601. Metal Steel Grade W-Nr X165CrMoV12 It is a die steel, use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold.

Applications

Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working

rolls , measuring tools .

Material equivalent of DIN X165CrMoV12 | 1.2601 steel

Germany	Italy	Sweden	Spain
DIN,WNr	UNI	SS	UNE
X165CrMoV12 \| 1.2601	X165CRMOW12KU	2310	X160CRMOV12

Chemical composition (wt.%) of 1.2601

C	Si ≤	Mn ≤	P ≤	S ≤	Cr	Mo	Other
1.55-1.75	0.25-0.40	0.20-0.40	0.030	0.030	11.0-12.0	0.50-0.70	V 0.10-0.50 W 0.40-0.60

Mechanical Properties of 1.2601

Rp0.2 (MPa)	Rm (MPa)	Impact KV (J)	Elongation A (%)	A Z (%)	Delivery	Hardness HB
641 (≥)	662 (≥)	23	14	31	Solution & Aging, Ann, Ausaging, Q+T	142

Heat treatment of X165CrMoV12 | 1.2601 Cold work tool steel

Annealing: Annealing temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255

Quenching: Hardening temperature/℃: 980~1010, Quenching in oil or air

Tempering: Commonly used drawing temperature/℃: 180~250; After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58

Normalizing：at Normalizing temperature, then cool in furnace