1.2360 X48CrMoV8-1-1 Cold Work Tool Steel

group name: Tool Steel Bars

Min Order: 1 piece

brand name: fushun

model: 1.2360 X48CrMoV8-1-1

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Tue, 25 Apr 2023 10:48:11 GMT

contact supplier

Paramtents

Delivery Condition +N or +A or +QT
Surface Condition black or turned or polished

Packging & Delivery

Min Order1 piece

Briefing

1.2360 X48CrMoV8-1-1 Cold Work Tool Steel ISO 9001 certified, On-time Delivery, Leading Global Supplier

Detailed

1.2360 X48CrMoV8-1-1 Cold Work Tool Steel

1.2360 X48CrMoV8-1-1 Alloy tool steel with increased chromium content, average strength, high hardness, ductility and high abrasion resistance. Used for precision woodworking tools - knives, blades, cutters, handles for the paper, wood, pulp, and paper industries, as well as cold forming tools. The increased content of vanadium provides a high hardenability, which makes it possible to achieve hardness within the limits of 60 HRC.

Applications

Blanking tools, stamping tools, embossing tools, forming dies, press dies, die inserts, extrusion dies, reinforcements, cold extrusion tools, tube tools, cutting tools, industrial knives, wood chipping knives, veneer knives.

Chemical composition % of the ladle analysis of grade 1.2360

C(％)	Si(％)	Mn(％)	P(％)	S(％)	Cr(％)	Mo(％)	V(%)
0.45-0.50	0.70-0.90	0.35-0.45	Max 0.020	Max 0.005	7.30-7.80	1.30-1.50	1.30-1.50

Mechanical properties of grade 1.2360

Proof strength Rp0.2(MPa)	Tensile strength Rm(MPa)	Impact energy KV(J)	Elongation at fracture A(%)	Reduction in cross section on fracture Z(%)	As-Heat-Treated Condition	Brinell hardness(HBW)
573(≥)	122(≥)	21	22	12	Solution and Aging,Annealing,Ausaging,Q+T,etc	311

Mechanical properities and heat treatment of steel 1.2360, X48CrMoV8-1-1:

Hardness in annealed condition <240 HB

Annealing in temperatures 835 - 865℃ cooling with furnace

Stress relief annealing at 650℃ cooling the furnace

Quenching at 1035 - 1070℃ with cooling in oil, salt bath or air

Tempering at temperatures 100 - 600℃