300M Alloy Steel Round Bars High Quality Suppliers

group name: Alloy Steel Bars

Min Order: 1 piece

brand name: fushun

model: 300M

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Mon, 01 Mar 2021 15:02:25 GMT

contact supplier

Paramtents

Delivery Condition normalised and tempered/softened

Packging & Delivery

Min Order1 piece

Briefing

300M Alloy Steel Round Bar's chemical component and applications. Fushun Metal is suppliers of 300M Alloy Steel Round Bars

Detailed

Introduce

300M is a high performance alloy steel which is a vacuum melted grade, supplied in the normalised and tempered/softened condition to enhance machinability prior to final heat treatment.

It has a combination of ultra high strength, good fatigue resistance and excellent transverse properties, and as such finds many applications in the aerospace industry, such as undercarriage components, gears and shafts.

Applications

300M can be used in a variety of applications, here are just a few examples:

*Undercarriage components

*Gears

*Shafts

*Aircraft landing gear

*High strength bolts

Standard

AMS 6417, ASTM A579

Properties

Density: 7.85 g/cm^3

Specific Heat Capacity: 448 J/kg*K

Coefficient of Thermal Expansion from -17.8-93°C: 11.34 µm/mm/°C

Chemical Component %

C	Si	Mn	P	S	Cr	Mo	Ni	V
0.38-0.46	1.45-1.8	0.6-0.9	0.01	0.01	0.7-0.95	0.3-0.65	1.65-2	0.05

Mechanical Properties

Mechanical & Physical Properties	21 °C
Ultimate Tensile Strength /MPa	1981
0.2% Yield Strength /MPa	1672
Reduction of area %	35
Elongation %	10
Room Temperature Hardness/ Rockwell C	58

(Normalised at 927 °C for 1 hour+air cool/Austenitised at 871°C for 1 hour + oil quench/Tempered at 302°C for 1 hour+air cool)

Hardness at Various Tempering Temperature	204°C	316°C	427°C	538°C	649°C
Hardness / Rockwell C	53	52.5	50	47	35

(Austenitised at 871°C for 1 hour + oil quench/Tempered for 2+2 hour+air cool)