Incoloy 800/800H/800HT N08811 N08810 N08800 1.4876 1.4959 Nickel Alloy Bar

group name: Nickel Alloy Bar

Min Order: 1 piece

brand name: fushun

model: Incoloy 800/800H/800HT N08811 N08810 N08800 1.4876

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Tue, 23 Jun 2020 10:48:02 GMT

contact supplier

Paramtents

Diameter Range 10-300mm
Length Range 1000-9000mm
Delivery Condition Annealed
Surface Condition Bright

Packging & Delivery

Min Order1 piece

Briefing

Incoloy 800 is an alloy of nickel, iron and chromium that maintaining austenitic after long time exposures to high temperatures

Detailed

Introduce

Incoloy 800 (UNS N08800, W. Nr. 1.4876) is a widely used material for construction of equipment requiring corrosion resistance, heat resistance, strength, and stability for service up to 1500°F (816°C). Alloy 800 offers general corrosion resistance to many aqueous media and, by virtue of its content of nickel, resists stress corrosion cracking. At elevated temperatures it offers resistance to oxidation, carburization, and sulfidation along with rupture and creep strength.

Applications

Incoloy 800 is used in a variety of applications involving exposure to corrosive environments and high temperatures. It is used for heat-treating equipment such as baskets, trays, and fixtures. In chemical and petrochemical processing, the alloy is used for heat exchangers and other piping systems in nitric acid media especially where resistance to chloride stress-corrosion cracking is required. In nuclear power plants, it is used for steam-generator tubing. The alloy is often used in domestic appliances for sheathing of electric heating elements. In the production of paper pulp, digester-liquor heaters are often made of alloy 800. In petroleum processing, the alloy is used for heat exchangers that air cool the process stream.

Standard

Rod, Bar, Wire, Forgings, and Forging Stock:

ASTM B 408, ASME SB 408 (Rod & Bar), ASTM B 564, ASME SB 564 (Forgings), ASME Code Case 1325 (All Product Forms), ASME Code Case 1949 (Forgings), AMS 5766 (Rod & Bar), ISO 9723 (Rod & Bar), ISO 9724 (Wire), ISO 9725 (Forgings), BS 3076NA15 (Rod & Bar), BS 3075NA15 (Wire), VdTÜV 412 (All Products).

Plate, Sheet, and Strip:

ASTM A 240, ASTM A 480, ASME SA 240, ASME SA 480 (Plate, Sheet, and Strip), ASTM B 409, ASTM B 906, ASME SB 409, ASME SB 906 (Plate, Sheet, and Strip), ASME Code Case 1325 (All Product Forms), ASME Code Case 2339 (Plate), AMS 5871 (Plate, Sheet, and Strip), BS 3072NA15 (Plate & Sheet), BS 3073NA15 (Strip), VdTÜV 412 (All Products), ISO 6208 (plate, sheet and strip).

Pipe and Tubes:

ASTM B 163 & ASME SB 163 (Seamless Condenser & Heat Exchanger Tubes), ASTM B 407, ASTM B 829, ASME SB 407, ASME SB 829 (Seamless Pipe & Tubes), ASTM B 514, ASTM B 775, ASME SB 514, ASME SB 775 (Welded Pipe), ASTM B 515, ASTM B 751, ASME SB 515, ASME SB 751(Welded Tubes), ASME Code Case 1325 (All Product Forms), ASME N-20 (Cold Worked Seamless Condenser and Heat Exchanger Tubes for Nuclear Service), BS 3074NA15 (Seamless Pipe & Tubes), VdTÜV 412 (All Products), ISO 6207 (Seamless Tubing).

Other Product Forms:

ASTM B 366 & ASME SB 366 (Fittings)

Chemical Composition

Grade	Al	C	Co	Cr	Cu	Fe	Mn	N	Ni	P	S	Si	Ti
Alloy 800	0.3	0.015	0.01	22	0.75	Bal	0.25	0.03	34	0.2	0.02	0.5	0.5

Mechanical Properties

Alloy	Form	Condition	Ultimate Tensile Strength, ksi (MPa)	Yield Strength at 0.2% offset, ksi (MPa)	Elongation in 2" or 4D, percent
800	Sheet, Plate	Annealed	85 (586)	40 (276)	43
800	Sheet, Plate Strip, Bar	Annealed	75 (520)*	30 (205)*	30*
800H	Sheet, Plate	SHT	80 (552)	35 (241)	47
800H	Sheet, Plate Strip, Bar	SHT	65 (450)*	25 (170)*	30*

Property

Machinability

Machining characteristics of this INCOLOY alloy 800 are similar to that of iron-based alloys. This alloy tends to work-harden during machining.

Welding

INCOLOY alloy 800 can be welded by common welding techniques, using a matching filler metal.

Forming

This alloy exhibits good ductility and hence can be formed using conventional methods.

Hot working

INCOLOY alloy 800 can be hot worked at temperature ranges of 871-1232°C (1600-2250°F).

Cold Working

Cold working may be done on the alloy using standard tooling.

Annealing

INCOLOY alloy 800 may be annealed after cold working. Annealing should be done at 982°C (1800°F) for 15 min and then the alloy should be air cooled.