1.2379 D2 SKD11 Cold Work Tool Steel

group name: Tool Steel Bars

Min Order: 1 piece

brand name: fushun

model: 1.2379 D2 SKD11 x153crmov12

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Thu, 14 Oct 2021 14:30:02 GMT

contact supplier

Paramtents

size range 5.5-500mm
shape round
Process hot rolled or hot forged
Delivery Condtion annealed
Surface Condition smooth, bright

Packging & Delivery

Min Order1 piece

Briefing

Fushun Supply 1.2379 D2 SKD11 Steel Round Bar: 5.5-500mm Diameter; Hot Rolled; Annealed; Bright Surface

Detailed

Introduce:

This material is used in punching, cold solid forming, deep drawing, coining and cold extrusion processing methods. During cold solid forming, materials are transformed into their final shape by cold forming or extrusion. Depending on the method employed, the forming tools can be exposed to extremely high wear resulting from pressure and abrasion.The coining or embossing process, especially the minting of coins, creates unusually high demands on the steels used for punches and dies when it comes to purity, compression strength and wear resistance.

In the mints where the coins are produced, even the slightest divergences relating to surface, dimensional or gravimetric accuracy result in the tools being taken out of service. This strongly underlines the importance of the tool steel quality employed.

Application

This material is used in the top heads and dies of machines that press metal materials. Small round steel bars made by hot rolling or forging have a good cold stamping capability.

Standard:

BS EN ISO 4957 Tool Steel

ASTM A681 Standard Specification for Tool Steel Alloy

Similar Grades:

ASTM	Material No.	DIN	EN
D2	1.2379	X155CrVMo12-1	X160CrMoV121

Chemical Composition:

Grade	C	Mn	Si	P	S	Cr	Mo	V
1.2379	1.45-1.6	0.20-0.60	0.10-0.6	0.03 max	0.03 max	11.0-13.0	0.7-1.0	0.7-1.0

Size & Process

Round Size Rnage:300-1000mm

Steel-making:EF/EAF+LF+VD EF/EAF+ESR

Process: Hot Rolleed or Hot Forged

Delivery condition: Annealed

Surface condition: Bright

Heat treatment:

Annealed(+A) max: 255HB
Annealing: slow cooling at 650ºC-850ºCfurnace
Quenching: Preheat 650ºC~750ºC increased to 1010ºC, air-cooled, or into the 996ºC to keep the salt bath, then cooled.
Tempering: The cold work D2 tool steel general tempering temperature is 170ºC-190ºC , Double tempering of Double tempering of D2 tool steel is recommended.