AISI 4145H 4145 G41450 SCM445 Alloy Steel Seamless Round Tube

AISI 4145H 4145 G41450 SCM445 Alloy Steel Seamless Round Tube
group name
Hollow Bars
Min Order
5 ton
brand name
fushun
Nearest port for product export
Tianjin, Qingdao, Shanghai, Huangshi
Delivery clauses under the trade mode
FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
Acceptable payment methods
T/T, L/C, D/P D/A
update time
Thu, 14 Oct 2021 14:30:33 GMT

Paramtents

  • Outer diameter 83-254 mm

  • Wall thickness 7 to 60 mm

  • length 12 meters

  • Cold drawn tolerance for OD and ID within ±0.2mm

  • Cold rolled tolerance for OD and ID within ±0.1mm

Packging & Delivery

  • Min Order5 ton

Briefing

AISI4145H Seamless Steel Tube used to Oil Exploration info..........com

Detailed

Application

This alloy is used in the oil and gas industry as forged down-hole drilling tools such as drill collars. Other applications are forged gears, shafts for hydraulic presses, rolls for paper mills, pump shafts and tool holders
Standard

Specifications

Standard:ASTM A519

Dimensions:Outer diameter: 83-254 mm, Wall thickness: 7 to 60 mm, length: not more than 12 meters.

Tolerance for OD and ID:
Cold drawn: within ±0.2mm
Cold rolled: within ±0.1mm

Tolerance for Wall Thickness:
Hot rolled: within +/-5%,
Cold drawn: within 0.6mm

Process:Hot Rolled, Cold Drawn, Precision Rolled
 
Delivery Condition:Hot rolled, Cold drawn, Annealed, Normalized, Quenched and tempered.

Surface Condition:Black surface, Rough turned, Peeled.

Chemical requirements: 

Grade

C

Mn

Pmax.

Smax.

Si

Cr

Mo

4145

0.43-0.48

0.75-1.0

0.04

0.04

0.15-0.35

0.80-1.10

0.15-0.25

AISI 4145H Steel Grade Heat Treatment
Annealing
Parts should be heated slowly to 1470-1560ºF ( 800 – 850ºC), soaked and furnace cooled to 900ºF (480ºC) then air cooled.

Normalizing
A typical normalizing temperature for 4145 forgings is 1600ºF (870ºC), but based on production experience this temperature may vary from 100ºF (38ºC) above to 50ºF (10ºC) below this figure. If normalizing is carried out before a hardening and tempering treatment, then the upper temperature range is used; if normalizing is the final treatment then the lower range is used.

Hardening
The austenitizing temperature for this grade is in the range 1500-1550ºF (815-845ºC). Parts should be slowly heated to this temperature, soaked and oil quenched. Parts should be tempered as soon as they reach room temperature.

Tempering
Parts will be tempered between 1020-1300ºF (550-700ºC) for 2 hours per inch (25 mm), then air cooled. Reduced impact values will be obtained on tempering at 500ºF (260ºC) or at 750 to 1025ºF (340 to 550ºC).
The optimum combination of strength and toughness is obtained from a microstructure that is tempered martensite. If very high strength is required then tempering is carried out at a low temperature – in fact this is a stress relief – when lightly-tempered martensite will result.
4145h steel