EN36C 832M13 1.6657 Case Harding Alloy Steel

group name: Alloy Steel Bars

Min Order: 1 ton

brand name: fushun

model: EN36C 832M13

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Tue, 12 Oct 2021 13:57:59 GMT

contact supplier

Paramtents

OD range: 80-800mm
Delivery condition: hot forged+QT+Black or Bright surface
Surface condition: Black
OD tolerance +/- 1-5%

Packging & Delivery

Min Order1 ton

Briefing

EN36C 832M13 1.6657 is nickel-chromium alloy case hardening steel that is specified for heavy duty highly-stressed applications

Detailed

Application of EN36C 832M13 1.6657:

EN36C 832M13 1.6657 can be used to make gear parts exposed to highest stresses and wear conditions. Typical components include gears, planet wheels, drive pinions, shafts, bushes and sleeves. Results in high core strength and excellent toughness in the components and is very suitable for parts with large diameter.

All Grades Comparison of EN36C 832M13 1.6657:

DIN	EN	ANFOR	BS
1.6657	14NiCrMo13-4	16NCD13	832M13 / EN36C

Quality Standard of EN36C 832M13 1.6657:

EN 10084 Case hardening steels
DIN17210 Case hardening steels
AS1444 Wrought alloy steels

Chemical Composition of EN36C 832M13 1.6657(%)

Steel Grade	C	Mn	Si	P	S	Cr	Ni	Mo
14NiCrMo13-4	0.11-0.17	0.30-0.60	0.40 max	0.025 max	0.025 max	0.80-1.10	3.00-3.50	0.20-0.30

Mechanical Properties of EN36C 832M13 1.6657: (T=20°C if not differently stated)

Process	Tensile Strength Rm (Mpa)	Elongation A5 (%)	Impact Value Kv (J) Room Temperature	Hardness (HB)
SOFT ANNEALED	/	/	/	217 max
QUENCHED AND TEMPERED	1230-1480	9 min	35 min	368-424

Heat treatment of EN36C 832M13 1.6657:

Soft Annealing: Heat EN36C to 825oC, cool slowly. This will produce a maximum Brinell hardness of 217.

Hardening: Harden from a temperature of 825-850oC, followed by oil or quenching.

Tempering:– After carburising and hardening, the steel is tempered between 140°C and 200°C as required.
For use in the non carburised heat treated condition, temper in accordance with properties required.