9254 Oil Hardened and Tempered Spring Steel Wires

group name: Oil Hardened and Tempered Spring Steel Wires

Min Order: 1 metric ton

brand name: fushun

model: 9254

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Thu, 30 May 2019 14:25:29 GMT

contact supplier

Paramtents

MOQ 1 Metric Ton
Quality Standard ASTM A29
Delivery Condition Oil Hardened and Tempered
Surface Condition Black suface,Blasted
Application Suspension Spring,Valve Spring
Delivery Time Within 30days

Packging & Delivery

Min Order1 metric ton

Briefing

9254 Oil Hardened and Tempered Spring Steel Wires are mainly used for Suspension Spring,Valve Spring.

Detailed

Products Details

1 High yield ratio, small spring residual deformation.

2 Stable performance: the difference of tensile strength in same coil is less than 60Mpa,which can extend the spring fatigue life.

3 The product rate after winding is high,which can reduce the cost. Oil quenching - tempering spring wire can not completely replace the cold-drawn spring wire. Especially the small size of the spring wire. Oil Hardened and Tempered spring wire is developed for the valve spring, suspension spring in fatigue resistance. And in order to achieve the best results, it should be combined with blasted process after winding. In recent years, with the improvement of the cognition level of this kind of product, this kind of product is gradually applied to clutch spring and car rigging.

Quality Standard

ASTM A29/A29M - 05 Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought,

Chemical Composition(%)

Steel Grade	C	Si	Mn	P	S	Cr
9254	0.51-0.59	1.20-1.60	0.60-0.80	0.035max	0.040 max	0.60-0.80

Mechanical Properties(Quenched and Tempered Condition)(T=20°C if not differently stated)

Steel Grade	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation A5 (%)	Area Reduction Ratio C (%)
9254	1450-1750	1300 min	6 min	25 min

Heat Treatment

Steel Grade	Quenching Temperature (°C)	Media	Tempering Temperature (°C)
9254	860	oil	450