100CrMn6 1.3520 High Carbon-Chromium Bearing Steel Round Bar

group name: Bearing Steel Bar

Min Order: 1 piece

brand name: fushun

model: 100CrMn6, 1.3520

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Mon, 22 Jun 2020 11:47:54 GMT

contact supplier

Paramtents

Diameter 20-180mm
Similar steel grades 100CrMn6, 1.3520
Delivery condition hot rolled+ spheroidizing annealing
Surface condition black, bright

Packging & Delivery

Min Order1 piece

Briefing

100CrMn6 1.3520 High Carbon-Chromium Bearing Steel Round Bar

Detailed

Introduction:

Professional manufacturer of asphalt machines. Our sales and R&D team have over 10 years’ experience to focus on asphalt distributor, synchronous pavement surface vehicles and other road machinery and equipment. Based on innovation

Quality Standard:

DIN 17230-1980 Ball and Roller Bearing Steels

All Grades Comparison:

Material No. 1.3520; EN 100CrMn6

Chemical Composition(%):

C	Si	Mn	P	S	Cr	Ni	Cu
0.90-1.05	0.50-0.70	1.00-1.20	0.030 max	0.025 max	1.40-1.65	0.30 max	0.30 max

Heat treatment:

l NORMALIZING: Normalizing temperature: 860-900℃.

l SOFT ANNEALING: Heat to 760-800℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 217.

l STRESS RELIEVING: Stress relieving to remove machining stresses should be carried out by heating to approx. 650℃, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

l HARDENING: Harden from a temperature of 830-890℃ followed by oil quenching. Hardness after quenching is approx. 64 HRC.

l TEMPERING: Tempering temperature: 150-180℃.