1.3343 Skh51 M2 W6Mo5Cr4V2 HSS High Speed Steel Round Bar

group name: High Speed Steel Bars

Min Order: 1 piece

brand name: fushun

model: 1.3343 / Skh51 / M2 / W6Mo5Cr4V2

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Tue, 12 May 2020 15:51:51 GMT

contact supplier

Paramtents

Surface condtion Smooth, Polished
Delivery Conditon Cold drawn+annealed
Similiar grade 1.3343 / Skh51 / M2 / W6Mo5Cr4V2
Standard BS EN ISO 4957 ASTM A600

Packging & Delivery

Min Order1 piece

Briefing

High Speed Steel(1.3343 / Skh51 / M2 / W6Mo5Cr4V2),HSS

Detailed

Introduction of M2 Steel:

1.3343 M2 steel is a general purpose molybdenum high speed steel. 1.3343/M2 steel is characterized by balanced combination of abrasion resistance, toughness and good red hardness. Due to its comparatively low carbon content, 1.3343/M2 steel has an excellent combination of toughness properties and abrasion resistance when properly hardened and tempered. 1.3343/M2steel is used in a wide used for all kinds of cutting tool, knife and punch and die applications.

Application of M2 Steel:

HSS Circular Saw, Blade, Press Mould, Drills, End mill, Planer Knife, Chipper Knife, Slice Knife, Hss Square Tool Bits.

This is a title

ASTM A600 1992 Standard Specification for High Speed Tool Steel

Chemical Composition of M2 Steel :

Steel Grade	C	Si	Mn	P	S	Cr	Mo	W	V
1.3343	0.86-0.94	0.45max	0.4max	0.03max	0.030max	3.8-4.5	4.7-5.2	5.9-6.7	1.7-2.4

Similar Grades: 1.3343 / Skh51 / M2 / W6Mo5Cr4V2

Shape:Round

Steel-making Process: EF/EAF+LF+VD, EF/EAF+ESR

Delivery condition: Cold Rolled+Annealed, Hot Rolled+Annealed.

Surface condition: Black, Smooth, Polished

Standard: BS EN ISO 4957, ASTM A600

Size Range: Dia:100mm max; Length:4000mm max

Tolerance of Amount: Above prices are based on actual weight.(+/-15%)

Machinability:

When properly annealed, M2 steel has a machinability rating of 65 percent when compared to a 1% Carbon Steel rated at 100.

Dimensional Stability:

When air quenched from the proper hardening temperature, this grade can be expected to expand approximately .001 in. per in. Note: Distortion (bending, bowing and twisting) and part geometry can add to the variations in movement of a part that is being hardened.

Thermal Cycling:

In order to avoid decarburization, this grade should be annealed in a controlled neutral atmosphere, vacuum, or neutral salt furnace environment.

1. Annealing: Heat to 1600° F, soak thoroughly at heat. Furnace cool 25° F per hour to 900° F, air cool to room temperature. Approximate annealed hardness 241 Maximum Brinell.