904L 1.4539 SUS904L Stainless Steel Bar

group name: Stainless Steel Bars

Min Order: 1 piece

brand name: fushun

model: DIN 1.4539 904L

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Thu, 14 Oct 2021 14:32:38 GMT

contact supplier

Paramtents

Delivery condition Harden
Surface Condition Smooth,black, bright
Shape round
Application oil and gas industries

Packging & Delivery

Min Order1 piece

Briefing

904L stainless steel is a non-stabilized austenitic stainless steel with low carbon content

Detailed

Introduction of 904L stainless:

904L stainless steel combines molybdenum and copper with iron for tremendously increased resistance to reducing acids like sulphuric acid. It stands up extremely well to chlorides in the environment for low pitting and crevice corrosion, as well as stress corrosion cracking.

Applications of 904L stainless:

904L stainless steel is widely used in the chemical, pharmaceutical, oil and gas industries. Typical applications include tanks, valves, heat exchangers, flanges and manifolds. The addition of copper to the composition of 904L stainless steel aids its suitability for components such as tanks and other products used in handling sulphuric and phosphoric acid.

Quality Standard of 904L stainless:

ASTM A182 Standard Specification for Forged or Rolled Alloy-Steel Pipe Flanges, Forged Fittings, and Valves and Parts
EN 10088 part3 stainless steel

STANDARD	WERKSTOFF NR.	UNS	JIS	AFNOR	BS	KS	EN
SS 904L	1.4539	N08904	SUS 890L	Z2 NCDU 25-20	904S13	STS 317J5L	X1NiCrMoCu25-20-5

Chemical Composition of 904L stainless (%):

Steel Grade	C	Si	Mn	P	S	Cr	Ni	Mo	Cu	N
904L	0.02 max	1.0 max	2.0 max	0.040 max	0.030 max	19.0-23.0	23.0-28.0	4.0-5.0	1.0-2.0	0.10 max
1.4539	0.02 max	0.7 max	2.0 max	0.040 max	0.010 max	19.0-21.0	24.0-26.0	4.0-5.0	1.2-2.0	0.15 max

Mechanical Properties of 904L stainless (Annealed)

Hardness (HB)	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation (%) (Long.)	Impact Value (J) (Long.)
230 max	530-730	230-260	35 min	100 min

Corrosion Resistance of 904L stainless:

Where a level of resistance to pitting corrosion better than 316 is required 904L stainless steel may be suitable. With its high nickel content at 25% it offers improved resistance to chloride stress corrosion cracking compared to other austenitic grades such as 304.