15-5PH 1.4545 Stainless Steel Bar

group name: Stainless Steel Bars

Min Order: 1 piece

brand name: fushun

model: 15-5PH

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Thu, 14 Oct 2021 14:44:23 GMT

contact supplier

Paramtents

Delivery condition harden
Surface Condition Smooth
Shape round
Application Aircraft components High pressure corrosive fabricated parts such as valves Shafts Fasteners Fittings and gears

Packging & Delivery

Min Order1 piece

Briefing

15-5 ph 1.4545 stainless steel is a martensitic, precipitation-hardening material with chromium, nickel and copper.

Detailed

Introduction of 15-5PH stainless:

15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.

15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.

Applications of 15-5PH stainless:

Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears

Quality Standard of 15-5PH stainless:

ASTM A564 2004 Standard Specification for Hot Rolled and Cold Finished Age Hardening Stainless Steel Bars and Shapes
ASTM A705 Standard Specification for Age Hardening Stainless Steel Forgings

All Grades Comparison of 15-5PH stainless:

DIN	ASTM	UNS	CNU
1.4545	XM-12	S15500	15-5PH

Chemical Composition of 15-5PH stainless(%)

C	Si	Mn	P	S	Cr	Ni	Cu	Nb+Ta
0.07 max	1.0 max	1.0 max	0.030 max	0.035 max	14.0-15.0	3.5-5.5	2.5-4.5	0.15-0.45

Mechanical Properties of 15-5PH stainless:

Delivery Condition	Modulus of Elasticity(GPa)	Modulus of Rigidity(GPa)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation % in 2″ (50.8 mm)	Reduction Of Area (%)	Hardness (HRC)
A(annealed)	/	/	/	/	/	/	35 max
H 900	197.6	77.3	1378 min	1276 min	14 min	50 min	44 min
H925	/	/	1309 min	1207 min	14 min	54 min	42 min
H1025	/	75.9	1173 min	1138 min	15 min	56 min	38 min
H1075	/	69	1138 min	1035 min	16 min	58 min	36 min
H1100	/	/	1035 min	931 min	17 min	58 min	34 min
H1150	/	69	1000 min	862 min	19 min	60 min	33 min