317L 1.4438 SUS317L Austenitic Stainless Steel

group name: Stainless Steel Bars

Min Order: 1 piece

brand name: fushun

model: 317L 1.4438 SUS317L

Nearest port for product export: Tianjin, Qingdao, Shanghai, Huangshi

Delivery clauses under the trade mode: FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF

Acceptable payment methods: T/T, L/C, D/P D/A

update time: Wed, 13 Oct 2021 14:12:13 GMT

contact supplier

Paramtents

Diameter 5-180mm
Delivery Condition Cold drawn only, Cold drawn+annealed.
Surface Condition bright, black

Packging & Delivery

Min Order1 piece

Briefing

Stainless steel grade 317L 1.4438 SUS317L Stainless Steel Round Bar is a low carbon version of grade 317 stainless steel.

Detailed

Standard

EN 10088-3: 2005 Stainless steels. Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes

EN 10028-7: 2007 Flat products made of steels for pressure purposes. Stainless steels

EN 10088-5: 2009 Stainless steels. Technical delivery conditions for bars, rods, wire, sections and bright products of corrosion resisting steels for construction purposes

JIS G4303 2005 Stainless steel bars

Chemical composition %

C	Si	Mn	Ni	P	S	Cr	Mo	N
max 0.03	max 1	max 2	13 - 16	max 0.045	max 0.015	17.5 - 19.5	3-4	max 0.11

Equivalent grades

EU	USA	Japan	France	England	Sweden	Finland
EN	-	JIS	AFNOR	BS	SS	SFS
X2CrNiMo18-15-4	317L	SUS317L	Z3CND19-15-04	317S12	2367	770

Size and Delivery Condition

Optional Process : Hot Rolled / Cold Drawn

Supply Round Diameter Range : 10-300 mm

Length Max 9 meters

Delivery Condition : Solution Annealed

Surface : Black / Ground / Polished

Mechanical properties

Rm - Tensile strength (MPa) (+A)	500-720
Rm - Tensile strength (MPa) (+AT)	490-690
Rp0.2 0.2% proof strength (MPa) (+A)	200-240
Rp0.2 0.2% proof strength (MPa) (+AT)	220
KV - Impact energy (J) transverse, (+A)	+20° / 60
KV - Impact energy (J) longitud., (+A)	+20° / 100
A - Min. elongation at fracture (%) (+A)	35-40
A - Min. elongation at fracture (%) longitud., (+AT)	35
Brinell hardness (HB): (+A)	215
Brinell hardness (HB): (+AT)	200